| Material: | Cr15mo |
|
Still deciding? Get samples of US$ 3.5/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
High Cr white iron:BTMCr15Mo,BTMCr20Mo,BTMCr26Mo:Hardness:≥HRC56,
Impact value:≥5J.
Quality Level:
As per National Standard & International Standards.
Production Process:
Sand Process With proper heat-treatment(quenching and tempering) process to achieve ideal hardness and impact value.
Standard Specification for High Cr Abrasion-resistant White Iron:
| Reference Standard (ISO 21988-2005) |
Nominal Chemical Composition (W%) | Eqv. Standards | |||||||||
| C | Si | Mn | Ni | Cr | Mo | Cu | P | S | |||
| ISO 21988/JN/ HBW555XCr13 |
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 11.0-14.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr11) ASTM A532 12% Cr |
|
| ISO 21988/JN/ HBW555XCr16 |
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 14.0-18.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr14) ASTM A532 15% Cr-Mo AS 2027 CrMo 15 3 G-X 300 CrMoNi 15 2 1 |
|
| ISO 21988/JN/ HBW555XCr21 |
1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 18.0-23.00 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr18) ASTM A532 20% Cr-Mo AS 2027 CrMo 20 1 G-X 260 CrMoNi 20 2 1 |
|
| ISO 21988/JN/ HBW555XCr27 |
1.8-3.6 | ≤1.0 | 0.5-2.0 | ≤2.0 | 23.0-30.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr23) ASTM A532 25% Cr-Mo AS 2027 Cr27 LC & Cr27 HC G-X 260 Cr27 |
|
| ISO 21988/JN/ HBW600XCr35 |
3.0-5.5 | ≤1.0 | 1.0-3.0 | ≤1.0 | 30.0-40.0 | ≤1.5 | ≤1.2 | ≤0.06 | ≤0.06 | AS 2027 Cr35 | |
| ISO 21988/JN/ HBW600XCr20Mo2Cu |
2.6-2.9 | ≤1.0 | ≤1.0 | ≤1.0 | 18.0-21.0 | 1.4-2.0 | 0.8-1.2 | ≤0.06 | ≤0.06 | AS 2027 CrMoCu 20 | |