Inconel718 alloy is a precipitation hardening nickel-chromium-iron alloy containing niobium and molybdenum. It has high strength, good toughness and corrosion resistance in high and low temperature environments below 650°C. The delivery state can be solid solution treatment or precipitation hardening state.
Warm up
The surface of the workpiece must be cleaned before and during the heating process to keep the surface clean. If the heating environment contains sulfur, phosphorus, lead or other low melting point metals, Inconel718 alloy will become brittle. Impurities come from marking paint, chalk, lubricating oil, water, fuel, etc. The sulfur content of fuel should be low. For example, the impurity content of liquefied gas and natural gas should be less than 0.1%, the sulfur content of city gas should be less than 0.25g/m3, and the sulfur content of petroleum gas should be less than 0.5%.
The heated electric furnace is suitable for more precise temperature control ability, the furnace gas must be neutral or weakly alkaline, and the composition of the furnace gas should be avoided from fluctuating in oxidizing and reducing properties.
Thermal processing
The suitable hot working temperature of Inconel718 alloy is 1120-900ºC, and the cooling method can be water quenching or other rapid cooling methods. After hot working, it should be annealed in time to ensure better performance. The material should be heated to the upper limit of the processing temperature during hot processing. In order to ensure the plasticity during processing, the final processing temperature when the deformation reaches 20% should not be lower than 960°C.
Cold working
Cold working should be carried out after solution treatment. The work hardening rate of Inconel718 is greater than that of austenitic stainless steel, so the processing equipment should be adjusted accordingly, and there should be an intermediate annealing process during the cold working process.
Heat treatment
Different solution treatment and aging treatment processes will result in different material properties. Due to the low diffusion rate of γ" phase, the mechanical properties of Inconel718 alloy can be obtained through long-term aging treatment.
Polished
The oxide near the weld of Inconel718 workpiece is more difficult to remove than stainless steel. It needs to be polished with a fine sanding belt. Before pickling in the mixed acid of and , the oxides should also be removed with sandpaper or salt bath pretreatment. deal with.
Machining
The machining of Inconel718 needs to be carried out after solution treatment, and the work hardening of the material should be considered. Unlike austenitic stainless steel, Inconel718 is suitable for low surface cutting speeds.
welding
The precipitation hardening type Inconel718 alloy is very suitable for welding and has no tendency to crack after welding. Weldability, ease of processing, and high strength are the major advantages of this material.
Inconel718 is suitable for arc welding, plasma welding, etc. Before welding, the surface of the material should be clean, free of oil, powder, etc., and the bright metal should be polished within 25mm of the weld.